Oxide scale formation - copper plated bolts




2003

We are plating copper on to steel bolts and passing through a furnace at a temperature of around 900°C.

The oxide scales are formed on the threads of the bolt.

We would like to use only copper based plating. Also enough care is taken in the process to close the furnace door during heating operation.

Is there any suggestion as how to eliminate the scale formation?

Ramachandran Rajagopal
- Bangalore, Karnataka, India




(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact  -  Privacy Policy  -  ©1995-2024 finishing.com, Pine Beach, New Jersey, USA  -  about "affil links"