Electro galvanizing Versus Hot Dip

We are erecting a boundary fence of wrought iron around our estate. The question is which method of galvanizing the wrought iron bars is best for the fence in the tropical climate that we experience in Singapore. Is it (a) electroplating (b) hot dip

Thanks,

Larry Henson
- Singapore
2003

Hot dip; it's no contest because the hot dip coating is thicker.

Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey
Need quick confidential answers? $25
Need project assistance? $100/hr.
2003

Sorry! Finishing.com is temporarily Read-Only.
Ted Mooney is retiring but I have several offers to take it over.
We're working hard to make sure we find it the best new home.

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: