Anodizing 6061 T6 vs. T651


(1998)

What affect will changing the temper condition for 6061 aluminum from T651 to T6 have on anodizing (sulfuric acid process, gold dye, hot water seal).

larry hanke
Larry Hanke
materials testing laboratory
Minneapolis, Minnesota




(1998)

If you are anodizing using current density, you should see no difference in the anodizing response of the two tempers.

Charlie Grubbs
- Alpharetta, Georgia


(1999)

What I am sending here is not a responce but a question asking for your help. Could you provide me with information about the density of 6005-T5 and 6061-T6 Aluminum alloys? Thanks for your cooperation. Ibrahim

Ibrahim Salau
aerospace - Jacksonville, Florida


(2000)

I aaam looking for some aluminium tubing 6061 T6 OD:.562X.035" WALL PLEASE ANYONE CAN HELP ME REGARDS DANIEL

DANIEL GAUTIER
- FT LAUDERdale, Florida



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.