Heat Treatment of 440 Stainless Steel





2002

I would like a federal standard or mil-std reference for Heat Treatment of 440 Stainless Steel.

James Howey
Cymer Inc. - San Diego, California, USA



2002

James,

Mil-H-6875 covered heat treating of Steel, and 440C is listed in Table 1B. A more current heat treating specification would be AMS 2759/5.

lee gearhart
Lee Gearhart
metallurgist - E. Aurora, New York


none
finishing.com is made possible by ...
this text gets replaced with bannerText
spacer gets replaced with bannerImages



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA