Dissolution of nickel from graphite

2002

Hi,

I want to dissolve and separate nickel from carbon. You said in nitric acid we can heat it at 80 deg. cent. is it possible to dissolve complete Nickel? If nickel is trapped inside the graphitic spherules, then how to dissolve it. what are the other methods?

Seeking for the require information urgently.

Vilas Pol
Barilan University - Ramatgan, Israel




2002

Lots of agitation and a very long time. Or burn the carbon at the lowest possible temperature. James Watts
- Navarre, Florida

help wanted ad
Plating Shop Manager [Salisbury, MD]
Junior Quality Engineer [Santa Clara, CA]
Plating Process Engineer [Wenatchee, WA]

Q, A, or Comment on THIS thread SEARCH for Threads about ... My Topic Not Found: Start NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2021 finishing.com, Pine Beach, New Jersey, USA