Ni/Au Immersion


(1998)

We are currently working on a set of problems regarding premature failures of electroless Ni/gold immersion pads and BGAs. We have seen a high O, C, with P and Ni that is black in color at the fractured sites. The bulk P content is approximately 5-6 atomic percent on bare boards but may slightly higher on the fracture surface, maybe 7 or 8. We have also seen, in a few instances, what appears to be (and for a lack of better terminology) a dual or two onion layer electroless Ni plating under the gold. The gold tends to be about 4 microinches and the Ni is > 200 microinches. I do know that ITRI and many others in the electronics industry are wrestling with this problem as we speak. What is the current understanding and information as to the cause of

The degraded solder joints that are made on some pads/BGAs after the Ni/Au platings? Second question is, what are the best techniques to quantitatively determine the porosity or void distribution/content of immersion gold coatings that are 3-6 microinches thick? Thanks for your consideration of my questions.

Harry Wachob
Exponent Failure Analysis Associates - Menlo Park, California


(1998)

I am not familiar with the BGA design. So my first question is, what is the substrate material for the Ni coating?

Mandar Sunthankar
- Fort Collins, Colorado



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.