topic 1517

Hard anodizing processes


I will appreciate if some one could help me with information on the following hard anodizing processes:

Scionic, Alpha and Imperv-X

Jean Rasmussen
- Rasmusen


We run the Imperv-x process & have been using it for 40+ years. It is great for coating hi copper alloys & for parts with sharp edges.

We also run the Mod Martin process for most of our "normal" Hardcoat work.

We have evaluated the Alpha process & we were not very impressed.

One of the newer processes we are using is the Anodal EE - and that is very impressive.

David A. Kraft
- Long Island City, New York

This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Comment to THIS thread START a NEW threadView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices

©1995-2018, Inc., Pine Beach, NJ   -   About   -  Privacy Policy
How Google uses data when you visit this site.