CAN I MAKE STAINLESS (300/400) FLAT BLACK OR GRAY AT HOME?





 

PLEASE, WHAT D.I.Y. PROCESS CAN I USE TO MAKE 300 AND 400 SERIES STAINLESS FLAT BLACK OR GRAY?

DALE ORNDORFF
- GRAND ISLAND, New York



 

Do you need an oxidation/anodization process or might some sort of paint or dye paint do, Dale?

Ted Mooney, finishing.com
Ted Mooney, P.E.
Striving to live Aloha
finishing.com - Pine Beach, New Jersey



 

Brown to black for SS:

13 gm Na2Cr2O7
1 lit H2SO4( 1,55 g/cm3)
temp. 18-25 C,5-10 min.

or

solution 2.(brown):

H2SO4(1,84 g/cm3).......50 ml/lit
Na2S2O3.................200 gm/lit
1 lit water,temp 30 °C

Goran Budija
- Cerovski vrh Croatia


adv.:   
anoplex banner



(No "dead threads" here! If this page isn't currently on the Hotline your Q, A, or Comment will restore it)

Q, A, or Comment on THIS thread -or- Start a NEW Thread

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

 
Jobshops
Capital
Equipment
Chemicals &
Consumables
Consult'g, Train'g
& Software


About/Contact    -    Privacy Policy    -    ©1995-2023 finishing.com, Pine Beach, New Jersey, USA