Gold colored chromium plating


(1998)

When I read the book Modern Electroplating on page 136 about Colored Chromium Deposits, I am very interested about topics of production 'Gold-colored' chromium deposit which is patented by The Corillium Corporation and marketed jointly with Harsaw Chemical Company.

My questions:

  1. Is the 'Gold-colored' chromium deposit the same plating process with some Hard Watchcase plating for example : Rado watchcase?
  2. What literature or book explains this case in more detail?
  3. How to contact the above companies?
  4. Is there other company selling or producing this kind of chemical?

Thanks to answer me

Anton Bijosono
PT.Citra Selaras Harmoni


(1998)

Harshaw is now Atotech, so that's a start. Other than that, plain chrome-colored chrome and black chrome are the only colors that I ever heard of; I'm not familiar with that gold colored chromium, but the very hard gold-colored material you see on such things as drill bits is titanium nitride, applied by vapor deposition, not gold chrome.

Ted Mooney, finishing.com Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey


Solar Power Your Home

(1998)

While you could get some information from the referenced patent, Atotech would be the route to go. Most colored bath are a pain to run and are very sensitive to current density which normally means shaped anodes or thieves. Real control will probably require instrumentation such as XRF. Might be an interesting hobby or sideline, but probably difficult to make a business out of it.

James Watts
- Navarre, Florida


(2001)

I am a student at Central Oregon Community College. I am gathering information for my engineering project. I would like to get information about the black chromium process. I am doing research on solar water heaters and their design and construction. I have learned that black chromium is very efficient in the heat absorption and transfer and has a very low loss. (0.95, 0.090) I would like to know how the process is done and any other pertinent information.

Keener, Lane
- Bend, Oregon


Nickel and Chromium Plating
Dennis & Such

There is very little difference in how black chromium is done from how conventional chrome plating is done. Just a "poison" in the bath that discolors it, and most of the major suppliers including Atotech offer it. Atotech calls it ChromOnyx®, I believe. But there is a lot involved in chrome plating.

Ted Mooney, finishing.com
Teds signature
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView This Week's HOT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.