Does phosphating hurt stainless steel?



A discussion started in 1995 & continuing through 2015

Phosphating of Metals
by Rausch

(1995)

Q. One of our clients suggests that zinc phosphate is detrimental to stainless steel. Can anyone tell me if this is the case?

M.F. de Keizer


(1995)

A. Hi M.F. As a rule, stainless steel cannot be successfully phosphatized. The metal is slightly attacked in phosphatizing, so it probably is correct to say it is "detrimental". However, the degree of attack is probably very low (phosphatizing tanks are made of stainless steel, and last decades). So we'd need to know a lot of details before being able to hazard an opinion as to whether it is actually harmful in a particular case.

pic of Ted Mooney
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey
Striving to live "Aloha"



(1995)

Q. Unfortunately I did not ask the right question. Hereby I will try again: My client suggests that when stainless steel is grit blasted with non-metallic grit and painted with a paint containing zinc phosphate, this paint could be detrimental to the stainless steel. Is there any documentation that can tell me if this is the truth? Thank you for any reply. Marcel

MF de Keizer (returning)


A. I hope someone else can shed some light on this, Marcel, because I have never heard of such a problem, and I am having difficulty envisioning how it could be harmful -- but I can't swear that it isn't :-(

pic of Ted Mooney
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey
Striving to live "Aloha"


January 8, 2013

A. Hello Mr MFK,

There is no issue in painting SS tanks with a zinc phosphate primer or a zinc chromate primer; the SS will not be attacked and the paint will serve well.

However, why not use a self etch primer instead first; they bond well onto SS and even onto nickel - chrome plating.

Follow up the self etching primer with a PU paint for a lifetime solution.

Khozem Vahaanwala
Khozem Vahaanwala
Saify Ind supporting advertiser
Bangalore, Karnataka, India

saify logo



To minimize searching and offer multiple viewpoints, we've combined multiple threads into the dialog you're viewing. Please forgive any resultant repetition or failures of chronological order.



How can stainless steel be phosphatized?

(2005)

Q. We are manufacturing rubber lined ss components. After sandblasting we are using Chemlok as bonding agent and directly we are doing rubber moulding. it is giving sufficient bond strength. some time any delay in processing causes rust over uncoated SS part.

Somebody suggested to go for phosphating so that the bond strength will improve as well as our rust problem will be solved. We have an idea like this about the process: First degreasing, then derusting, then chromating , then activation , phosphating and then passivation. We don't know the material and composition that can be used for this purpose. We know ZnO, phosphoric acid and nitric acid are used in this operation. Anybody can give more info?
Regards,

Ashok Kumar
- Mumbai, Maharashtra, India


(2005)

A. I don't know of any way that S.S. can be phosphated.

Brian C. Gaylets
- Scranton, Pennsylvania


(2005)

A. Rusting of stainless after sandblasting is usually due to iron contamination of the sand -- from cleaning steel, cast iron grit, etc. Use clean sand or else follow by cleaning and passivation per ASTM A380 [link is to the practice at TechStreet] .

What is the composition of Chemlok? Etchants, especially those with ferric chloride, can cause rusting.

Ken Vlach
- Goleta, California
contributor of the year

Finishing.com honored Ken for his countless carefully
researched responses. He passed away May 14, 2015.
Rest in peace, Ken. Thank you for your hard work
which the finishing world continues to benefit from.



(2005)

A. Why use stainless if you're going to alter the surface? Why don't you use a cheaper material if you have to go through so much prep and are destroying the mechanical properties of the stainless in the process?

Sheldon Taylor
Sheldon Taylor
   supply chain electronics
Wake Forest, North Carolina



(2005)

A. Cathodic electrochemical treatment can be used to deposit a phosphate based coating on stainless steels. The electrolyte solution consists of a zinc salt, phosphoric acid and an accelerator. The deposit on stainless steel will be a zinc - zinc phosphate composite coating.

T.S.N. Sankara Narayanan
T.S.N. Sankara Narayanan
- Chennai, Tamilnadu, India
(ed.note Nov. 2017: The good doctor has a fascinating blog at https://advancementinscience.wordpress.com)


December 11, 2012

Q. Hi,

I have some technical questions regarding Zinc phosphate. It will be very much appreciated your reply as soon as possible.

We are putting around 5% (w/w) Zinc sulphate in one Metal cleaner formula and we are going to fill the bottles through a stainless steel filler.

My question is whether there is any possibility that the stainless steel filler will be permanently coated with Zinc Phosphate? If coated, how can it be removed because the same filler pipe is used for other products (we are concerned about cross contamination).

Masudun Nabi
- Montreal, QC. Canada


January 8, 2013

A. A mild Nitric acid wash will clean SS quite well. Please rinse well afterwards.

Khozem Vahaanwala Khozem Vahaanwala
Saify Ind 
Bangalore, Karnataka, India



June 26, 2015 -- this entry appended to this thread by editor in lieu of spawning a duplicative thread

Q. Is there any typical phosphating cycle for 304L stainless steel?

Maruti Dandwate
- mumbai, Maharashtra, India


June 2015

thumbs up signHi, Maruti. Sankara has answered your question, but each time people ask it, we all ask in return "Why?" :-)

So please return the favor by telling us why you would want to phosphatize stainless steel. Thanks!

Regards,

pic of Ted Mooney
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey
Striving to live "Aloha"

July 1, 2015

Q. Phosphatizing is our client requirement. However, at this stage we do not have any details of phosphatizing. Hence I am asking if there is any typical cycle for an equipment with SS304L material.

Maruti Dandwate [returning]
- Mumbai, Maharashtra, India


July 2015

A. Hi again Matuti.

Okay, then we must ask: "Are you sure that your client knows what they are doing?" :-)
... because this situation introduces the frequently repeated question of who is supposed to be the expert.

If an aircraft or automobile manufacturer specifies a process, it is your obligation as the plating shop to simply do what they ask because they are the experts -- although it might still be prudent to inquire about it if it sounds off the wall to you. At the other extreme if a consumer asks you to process a part, you are the expert that he came to and relied on; so if he asked for something stupid it's your obligation to educate him. In your case, as we've already said, we don't understand why your client would want to phosphatize stainless steel, and suspect that it may be an error or misunderstanding.

We know that phosphatizing of 304L stainless steel can't be done via the process commonly recognized as phosphatizing, but that a zinc-zinc phosphate coating can be achieved through a special electrochemical process explained by Sankara. Good luck in talking to your client about it.

Regards,

pic of Ted Mooney
Ted Mooney, P.E. RET
finishing.com
Pine Beach, New Jersey
Striving to live "Aloha"



This public forum has 60,000 threads. If you have a question in mind which seems off topic to this thread, you might prefer to Search the Site

ADD a Q or A to THIS thread START a NEW THREADView CURRENT TOPICS

Disclaimer: It's not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations may be deliberately harmful.

  If you need a product/service, please check these Directories:

JobshopsCapital Equip. & Install'nChemicals & Consumables Consult'g, Train'g, SoftwareEnvironmental ComplianceTesting Svcs. & Devices


©1995-2017 finishing.com     -    Privacy Policy
How Google uses data when you visit this site.