What is zinc ash and bottom dross loss?

        

+++++++

What is the normal ratio of the Zinc ash and bottom dross compared with the consumed Zinc in hot dip galvanization and how I can recover pure Zinc from the ash and dross effectively. I am a manager and producing galvanized wire by hot dip process and the Zinc lost through dross and ash is really bothering me much.So far I remelted the ash (big sizes) in a curicible and recovered metallic Zinc.I have also used ammonium chloride but not found very effective.How can I increase the effectiveness.Is there other additives to mix with the ash and dross?
If you could give me some recommentation it will be very appreciated.

Süleyman BEÞLÝ
ÖZYAÞAR A.Þ - Silivri-ISTANBUL, TURKEY


+++++++

Could you please answer how I can reduce the smoke(fume) created during hot dip galvanization on the Zinc furnace and reduce the zinc ratio retained in the ash?

Süleyman BEÞLÝ
--ISTANBUL, TURKEY

ANSWER or FOLLOW UP POST an unrelated QUESTION HOT Topics

Disclaimer: It is not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information
presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The
internet is largely anonymous; some names may be fictitious and some recommendations may be deliberately harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Jobshops Capital Equip. & Install'n Chemicals & Consumables Consult'g, Train'g, Software Environmental Compliance Testing Svcs. & Devices Used & Surplus


Home    -    Contact    -    ©1995-2012 finishing.com     -    Privacy    -    Search