Sheradising

An alternative to zinc electro-, mechanical, paint coatings that you don't hear much about, is sheradising. What is the optimal size (um) for the zinc powder used? Out of interest, are any analogous processes for coating with material other than zinc available?

Terry Roberts
- Australia
1999

2000

Dear Mr. Roberts,

there is a new process which is a little bit similar to sheradising. It is called ZN�. In this process only ZN powder is used (no sand). Process time is less.

Best regards,

Peter Kordt
- Hagen, Germany

Sorry! Finishing.com is temporarily Read-Only.
Please maintain your bookmarks! Although Ted Mooney is retiring, finishing.com is not!
It will have a new owner/curator very shortly!

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: