Ti6Al4V Anodizing versus Fatigue behavior

We know that the anodizing on aluminum alloys decreases the fatigue life of the parts. The sulfuric acid anodizing is more susceptible to fatigue than chromic acid anodizing. I would like to know if the sulfuric acid on Ti6Al4V, decreases the fatigue life

With my Best Regards,

Rogério de Almeida Silva
Embraer - São José dos Campos, São Paulo, Brazil
2003

Sorry! Finishing.com is temporarily Read-Only.
Ted Mooney is retiring but I have several offers to take it over.
We're working hard to make sure we find it the best new home.

Disclaimer: It's not possible to fully diagnose a finishing problem or the hazards of an operation via these pages. All information presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The internet is largely anonymous & unvetted; some names may be fictitious and some recommendations might be harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: