7050T7451 Corrosion Tests

     

+++++

I am having problems with my anodize passing salt spray tests. I would like to get additional info if possible.

1. We have fabricated our test samples our to plate. Is there a difference between running the samples made of extrusion vs plate in this alloy?
2. I have noticed a pattern in the samples after etch and anodize. It is confined to 1 face of the samples. When I run my finger nail over the areas there is a definite hang. Any thoughts on the condition?

Bob Potter
metal finishing - Wichita, KS, USA


ANSWER or FOLLOW UP POST an unrelated QUESTION HOT Topics

Disclaimer: It is not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information
presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The
internet is largely anonymous; some names may be fictitious and some recommendations may be deliberately harmful.

If you are seeking a product or service related to metal finishing, please check these Directories:

Jobshops Capital Equip. & Install'n Chemicals & Consumables Consult'g, Train'g, Software Environmental Compliance Testing Svcs. & Devices Used & Surplus


Home    -    Contact    -    ©1995-2012 finishing.com     -    Privacy    -    Search