Aluminum cathodes for anodizing

+++

What is the best alloy of aluminum to use for cathode in an anodizing tank(sulfuric acid).

Vick Corso
fabtricators - Slidell, LA, U.S.

+++

6063 T6. For more info see letter 1177.

Ted Mooney, P.E.
finishing.com
Brick, New Jersey

+++

The alloy of choice is 6063t6. It is the most durable Aluminum alloy for sulfuric acid anodizing baths,both type II and III hard coat. We have system using this alloy in the field for over 2 1/2 years with minimal material loss even without cathode protection. Although there is some difference of opinion on the matter we prefer the flexibility of bolted connections. Attend the talk at Sur/Fin on equipment updates in anodizing in Milwaukee in June.

Drew Nosti CEF
Member AESF Light Metal Committee
Member AAC Hard Coat Committee

Drew Nosti, CEF
Ladson, South Carolina

ANSWER or FOLLOW UP POST an unrelated QUESTION HOT Topics

Disclaimer: It is not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information
presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The
internet is largely anonymous; some names may be fictitious and some recommendations may be deliberately harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: