Sample prep for SEM

My company has recently upgraded our SEM, and we wish to start looking at the pores of an anodized coating (H2S04). To this point we have had very little success. Can someone reccomend proper sample preparation? The SEM is capable of 100k magnification, so we believe that we should be able to look at the porous structure of the coating.

Thanks in advance for any advice.

Marc Green
anodizer - Boise, Idaho

First of two simultaneous responses -- ++

I'm not sure about an anodized surface, but when I was playing with SEM and circuit boards I always gold sputtered them.

James Totter, CEF
- Tallahassee, Florida

Second of two simultaneous responses -- ++

Marc, are you using an environmental SEM (one of those you can backfill with a low pressure of gas to bleed off charge, then use backscatter imaging) or are you coating with gold? I'd suspect the sputter coating with gold would be a better method, as secondary imaging has a lot more resolution than backscatter.

If you want to send me a sample, I'll look at it in our SEM (Amray 3200, with environmental mode- but we've kept our sputter coater) and e-mail you some photos. [Contact information has been sent in private.]

Lee Gearhart
metallurgist
East Aurora, New York

ANSWER or FOLLOW UP POST an unrelated QUESTION HOT Topics

Disclaimer: It is not possible to diagnose a finishing problem or the hazards of an operation via these pages. All information
presented is for general reference and does not represent a professional opinion nor the policy of an author's employer. The
internet is largely anonymous; some names may be fictitious and some recommendations may be deliberately harmful.

If you are seeking a product or service related to metal finishing, please check these Directories: