Anybody have any info they would care to share about composite electroplating? Specifically:

- the ceramic to be co-deposited in this particular case is silicon carbide. Do people usually pretreat this powder in some specific fashion?

- in addition to the nickel plating solution and the usual additives, are any sort of thixotropic or viscosity-enhancing agents ever added to the solution?

- is there a current density that is too high or too low for good co-deposition?

 
Ted Mooney, P.E.
finishing.com - Brick, NJ

Regarding the composite electroplating, especially Ni-SiC composite, Malathy Pushpavanam and her colleagues at Central Electrochemical Research Institute, Karikudi, India seem to have done some work. Her article, "Nickel-Boron Nitride Electrocomposites" pubilshed in Metal Finishing, p. 97, June 1995, mentions her earlier work on Ni-SiC composites (references 4 and 5 in this paper). Also, the techniques she followed were described in references 3-6. Reference 3 is a paper published in Metal Finishing, vol. 30(4), p. 39, 1974. Unfortunately, I do not have copies of her other articles.

Hope this info is of some use to you.

Currently, we are also looking in to this electrocomposite plating and plating of tungsten carbide particles. With respect to the tungsten carbide particles, we had some success with gold deposition. It is still in experimental stage at this time. We will keep you posted of our success.

Thanking you,

Dr. Kamal Murthy

I do have a copy of a pretty good paper called "Electrochemical codeposition of inert particles in a metallic matrix" published in the journal of applied electrochemistry, it lists about 56 references at the end, I can fax a copy if you think it might help, just let me know your fax no.
There is also a proprietory process called "Nikasil" on the market, this is an electrolytic nickel silicon carbide process, I think its supplied by LPW in germany, its used in europe on motorcycle cylinder bores etc. Hope this helps

Regards
Richard

PS Like the hot line great idea, its a good way to chill out just browsing after a hard day at the tank side (are'nt thy all!)

Richard Guise
MP (eastern) Ltd

Ted,

Are you still interested in this subject. Worked for a number of years with chromium carbide deposited out of a cobalt sulfate and there are a number of things that are helpful in keeping it plating.

James Watts - Fl

 
Ted Mooney, P.E.
finishing.com - Brick, NJ

You're asking three questions.

For the1st question, you have to pretreat your carbide powder for a good wetting by water (in alkaline solution, for example), and, if you want to use the SiC dissolution in nickel (up to 650°C), you have to pretreat your powder in a fluorhydric solution to dissolve the SiO2 gangue.

It is possible to have a viscosity-enhancing by use of acrylic acid partially polymerized and stabilizated by Fe. This product is commercially available under the name "COATEX P 90" (Idon't know the distributor in the USA).

For the 3d question Guglielmi is giving the answer in "Kinetics of the deposition of inert particles from electrolytic baths" (J. Electrochem. Soc., 119, 8, 1009-1012 ; aug. 1972). This work was confirmed by J.R. Roos et al. in the 10th Int. Cong. Met. Finish., Proc., 203-207 (1980), by C. Buelens et al. ("Electrochemical aspects of the codeposition of gold ans copper with inert particles", J. Applied Electrochem., 13, 541-548, 1983). You can also read some papers written by P.K. Sinha et al. (plating, 60, 1, 55-59 ; 1973), M. Pushpanavan et al. (Met. Finish., 38-43 ; 1977), and so on
....

All these papers mentionned the relation between the state of polarization of the cathod (or, if you prefer, the current density) and the particle size. In my experience, it is possible to extend the Guglielmi model to the composite electroless deposits (in this case too, it is easy to define the tafel's beta lines and to have a preview of the quantity of inert particles include in the deposit). I'd patented this technology in 1986 (us pat. 4 844 739) without any explanation.

I hope these informations were some use for you. My appologies for my bad english.

Best regards.

P.S. What a good idea this hot line ! Now I'm sure I can help somebody or somebody can help me in my research. Thanks to finishing.com.

Pierre Josso -
Office National d'Etudes et de Recherches Aerospatiales (ONERA)
ONERA - Materials Science Department
BP 72 - 92322 Chatillon - France

Thanks for the great response, Pierre!

 
Ted Mooney, P.E.
finishing.com - Brick, NJ

I would like to know if anyone is "brush" plating any of these composite chemistries, in particular the "nikasil" refered to.

There seems to be several companies scattered around the US using nikasil as a means of salvage of motorcycle (and snowmobile) cylinder bores. I am interested in finding a supplier for the chemical solutions, the preplate steps involved, and anyone having any information regarding the possibility of application by the "brush" or selective method

Robin McCullough -
Endos

Letter 1671 deals with Nikasil, and includes links to several other letters which also do.

 
Ted Mooney, P.E.
finishing.com - Brick, NJ

I want to post a question or inquiry of my own.

 

I want to answer or follow-up on this question publicly

 

This letter is within a monitored forum, very much "alive" here in 2008. If you spot any broken links or obsolete info, please advise!